100% Original Cu15ni8sn Foil - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou
100% Original Cu15ni8sn Foil - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:
1. Chemical Composition of C72700
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
Density |
8.9 |
(g/cm3) |
Melting Point |
968-1078 |
(℃) |
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
Elastic Modulus |
120 |
(GPa) |
Electrical Resistivity at 20℃ |
|
μΩ*cm |
Quench |
≤19.5 |
|
Precipitation Hardening |
≤15 |
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
≥9 |
|
|
Precipitation hardening(3 hours) |
≥12 |
|
Torsional Modulus |
50 |
(GPa) |
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
Quenching |
||||||||
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
Quenching/Cold Rolling |
||||||||
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
Quenching/Precipitation Heat Treatment |
||||||||
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
2) Drawn products
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching |
|||||
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
Quenching/Cold Rolling |
|||||
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
Quenching/Precipitation Heat Treatment |
|||||
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
inch |
mm |
inch |
mm |
inch |
mm |
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation<0.25 inches |
length=3048mm,deviation<6.35mm |
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation<0.5 inches |
length=3048mm,deviation<12mm |
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
<0.4 |
<10 |
+/-0.002 |
+/-0.05 |
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts
Product detail pictures:
Related Product Guide:
Our products are broadly regarded and reliable by end users and can meet up with constantly transforming financial and social requires of 100% Original Cu15ni8sn Foil - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: Italy, Macedonia, Morocco, They are sturdy modeling and promoting effectively all over the world. Never ever disappearing major functions within a quick time, it's a have to for you of fantastic good quality. Guided by the principle of Prudence, Efficiency, Union and Innovation. the corporation. ake an excellent efforts to expand its international trade, raise its organization. rofit and raise its export scale. We are confident that we are going to have a bright prospect and to be distributed all over the world in the years to come.
By Murray from New Zealand - 2018.12.30 10:21
Cooperate with you every time is very successful, very happy. Hope that we can have more cooperation!
By Ella from Zimbabwe - 2018.05.22 12:13