2020 High quality Cuco2be Tube - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou
2020 High quality Cuco2be Tube - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:
1. Chemical Composition of C72700
|
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
|
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
|
Density |
8.9 |
(g/cm3) |
|
Melting Point |
968-1078 |
(℃) |
|
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
|
Elastic Modulus |
120 |
(GPa) |
|
Electrical Resistivity at 20℃ |
|
μΩ*cm |
|
Quench |
≤19.5 |
|
|
Precipitation Hardening |
≤15 |
|
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
|
≥9 |
|
|
|
Precipitation hardening（3 hours） |
≥12 |
|
|
Torsional Modulus |
50 |
(GPa) |
|
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
|
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
|
Quenching |
||||||||
|
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
|
Quenching/Cold Rolling |
||||||||
|
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
|
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
|
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
|
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
|
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
|
Quenching/Precipitation Heat Treatment |
||||||||
|
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
|
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
|
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
|
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
|
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
|
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
|
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
||||||||
2) Drawn products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
|
Quenching |
|||||
|
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
|
Quenching/Cold Rolling |
|||||
|
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
|
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
|
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
|
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
|
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching/Precipitation Heat Treatment |
|||||
|
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
|
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
|
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
|
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
|
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
|
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
|
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
|
inch |
mm |
inch |
mm |
inch |
mm |
|
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation＜0.25 inches |
length=3048mm,deviation＜6.35mm |
|
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
|
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation＜0.5 inches |
length=3048mm,deviation＜12mm |
|
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
|
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
|
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
|
＜0.4 |
＜10 |
+/-0.002 |
+/-0.05 |
|
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts
Product detail pictures:
Related Product Guide:
we could supply good quality goods, aggressive cost and very best purchaser assistance. Our destination is "You come here with difficulty and we supply you with a smile to take away" for 2020 High quality Cuco2be Tube - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: Hungary, Uzbekistan, Hyderabad, Since the establishment of our company, we've realized the importance of providing good quality goods and the best before-sales and after-sales services. Most problems between global suppliers and clients are due to poor communication. Culturally, suppliers can be reluctant to question points they do not understand. We break down these barriers to ensure you get what you want to the level you expect, when you want it.
By Andrea from South Africa - 2018.12.11 14:13
The accounts manager made a detailed introduction about the product, so that we have a comprehensive understanding of the product, and ultimately we decided to cooperate.
By Annie from Azerbaijan - 2017.09.16 13:44