Bottom price Beryllium Copper Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou
Bottom price Beryllium Copper Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:
1. Chemical Composition of C72700
|
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
|
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
|
Density |
8.9 |
(g/cm3) |
|
Melting Point |
968-1078 |
(℃) |
|
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
|
Elastic Modulus |
120 |
(GPa) |
|
Electrical Resistivity at 20℃ |
|
μΩ*cm |
|
Quench |
≤19.5 |
|
|
Precipitation Hardening |
≤15 |
|
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
|
≥9 |
|
|
|
Precipitation hardening（3 hours） |
≥12 |
|
|
Torsional Modulus |
50 |
(GPa) |
|
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
|
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
|
Quenching |
||||||||
|
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
|
Quenching/Cold Rolling |
||||||||
|
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
|
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
|
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
|
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
|
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
|
Quenching/Precipitation Heat Treatment |
||||||||
|
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
|
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
|
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
|
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
|
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
|
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
|
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
||||||||
2) Drawn products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
|
Quenching |
|||||
|
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
|
Quenching/Cold Rolling |
|||||
|
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
|
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
|
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
|
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
|
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching/Precipitation Heat Treatment |
|||||
|
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
|
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
|
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
|
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
|
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
|
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
|
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
|
inch |
mm |
inch |
mm |
inch |
mm |
|
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation＜0.25 inches |
length=3048mm,deviation＜6.35mm |
|
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
|
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation＜0.5 inches |
length=3048mm,deviation＜12mm |
|
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
|
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
|
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
|
＜0.4 |
＜10 |
+/-0.002 |
+/-0.05 |
|
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts
Product detail pictures:
Related Product Guide:
Our corporation puts emphasis about the administration, the introduction of talented staff, plus the construction of team building, attempting hard to improve the quality and liability consciousness of team members. Our organization successfully attained IS9001 Certification and European CE Certification of Bottom price Beryllium Copper Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: Maldives, Colombia, Milan, Only for accomplishing the good-quality product to meet customer's demand, all of our products have been strictly inspected before shipment. We always think about the question on the side of the customers, because you win, we win!
By Yannick Vergoz from Bahrain - 2018.06.19 10:42
Good quality, reasonable prices, rich variety and perfect after-sales service, it's nice!
By ROGER Rivkin from Nepal - 2018.07.26 16:51