Factory Free sample China 2.5m 3m Solid Beryllium Copper/Bronze Bar Rod
Our pursuit and enterprise aim would be to “Always fulfill our buyer requirements”. We carry on to acquire and layout excellent quality items for the two our old and new clients and realize a win-win prospect for our shoppers in addition as us for Factory Free sample China 2.5m 3m Solid Beryllium Copper/Bronze Bar Rod, Standing still today and seeking into the longer term, we sincerely welcome customers all over the environment to cooperate with us.
Our pursuit and enterprise aim would be to “Always fulfill our buyer requirements”. We carry on to acquire and layout excellent quality items for the two our old and new clients and realize a win-win prospect for our shoppers in addition as us for C17300 C17510 C17200, Our advantages are our innovation, flexibility and reliability which have been built during last 20 years. We focus on providing service for our clients as a key element in strengthening our long-term relationships. The continual availability of high grade products in combination with our excellent pre- and after-sales service ensures strong competitiveness in an increasingly globalized market.
1. Chemical Composition of C72700
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
Density |
8.9 |
(g/cm3) |
Melting Point |
968-1078 |
(℃) |
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
Elastic Modulus |
120 |
(GPa) |
Electrical Resistivity at 20℃ |
|
μΩ*cm |
Quench |
≤19.5 |
|
Precipitation Hardening |
≤15 |
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
≥9 |
|
|
Precipitation hardening(3 hours) |
≥12 |
|
Torsional Modulus |
50 |
(GPa) |
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
Quenching |
||||||||
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
Quenching/Cold Rolling |
||||||||
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
Quenching/Precipitation Heat Treatment |
||||||||
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
2) Drawn products
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching |
|||||
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
Quenching/Cold Rolling |
|||||
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
Quenching/Precipitation Heat Treatment |
|||||
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
inch |
mm |
inch |
mm |
inch |
mm |
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation<0.25 inches |
length=3048mm,deviation<6.35mm |
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation<0.5 inches |
length=3048mm,deviation<12mm |
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
<0.4 |
<10 |
+/-0.002 |
+/-0.05 |
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning partsOur pursuit and enterprise aim would be to “Always fulfill our buyer requirements”. We carry on to acquire and layout excellent quality items for the two our old and new clients and realize a win-win prospect for our shoppers in addition as us for Factory Free sample China 165mm 90mm 80mm 100mm Solid Beryllium Copper/Bronze Bar Rod, Standing still today and seeking into the longer term, we sincerely welcome customers all over the environment to cooperate with us.
Factory Free sample China Copper Rod, Our advantages are our innovation, flexibility and reliability which have been built during last 20 years. We focus on providing service for our clients as a key element in strengthening our long-term relationships. The continual availability of high grade products in combination with our excellent pre- and after-sales service ensures strong competitiveness in an increasingly globalized market.