Factory source C17500 Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou
Factory source C17500 Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:
1. Chemical Composition of C72700
|
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
|
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
|
Density |
8.9 |
(g/cm3) |
|
Melting Point |
968-1078 |
(℃) |
|
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
|
Elastic Modulus |
120 |
(GPa) |
|
Electrical Resistivity at 20℃ |
|
μΩ*cm |
|
Quench |
≤19.5 |
|
|
Precipitation Hardening |
≤15 |
|
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
|
≥9 |
|
|
|
Precipitation hardening（3 hours） |
≥12 |
|
|
Torsional Modulus |
50 |
(GPa) |
|
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
|
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
|
Quenching |
||||||||
|
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
|
Quenching/Cold Rolling |
||||||||
|
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
|
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
|
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
|
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
|
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
|
Quenching/Precipitation Heat Treatment |
||||||||
|
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
|
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
|
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
|
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
|
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
|
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
|
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
||||||||
2) Drawn products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
|
Quenching |
|||||
|
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
|
Quenching/Cold Rolling |
|||||
|
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
|
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
|
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
|
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
|
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching/Precipitation Heat Treatment |
|||||
|
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
|
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
|
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
|
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
|
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
|
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
|
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
|
inch |
mm |
inch |
mm |
inch |
mm |
|
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation＜0.25 inches |
length=3048mm,deviation＜6.35mm |
|
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
|
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation＜0.5 inches |
length=3048mm,deviation＜12mm |
|
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
|
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
|
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
|
＜0.4 |
＜10 |
+/-0.002 |
+/-0.05 |
|
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts
Product detail pictures:
Related Product Guide:
We are going to make every single effort for being excellent and excellent, and accelerate our ways for standing while in the rank of international top-grade and high-tech enterprises for Factory source C17500 Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: London, Malaysia, UK, When It produced, it making use of the world's major method for reliable operation, a low failure price, it appropriate for Jeddah shoppers choice. Our enterprise. s situated inside the national civilized cities, the website traffic is very hassle-free, unique geographical and financial circumstances. We pursue a "people-oriented, meticulous manufacturing, brainstorm, make brilliant" company philosophy. Strict good quality management, fantastic service, affordable cost in Jeddah is our stand around the premise of competitors. If needed, welcome to make contact with us by our web page or phone consultation, we'll be delighted to serve you.
By Eric from Buenos Aires - 2017.07.07 13:00
Although we are a small company, we are also respected. Reliable quality, sincere service and good credit, we are honored to be able to work with you!
By Marjorie from British - 2018.06.12 16:22