China Factory Supply Cuco2be Foil - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou factory and suppliers

Factory Supply Cuco2be Foil - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou

Product Detail

Product Tags

Feedback (2)

Our advancement depends over the highly developed devices, excellent talents and continually strengthened technology forces for Cuni1co1be Foil , C17200 Beryllium Copper , C17200 Beryllium Copper Heat Treatment , Our tenet is "Reasonable prices, efficient production time and best service" We hope to cooperate with more customers for mutual development and benefits.

Factory Supply Cuco2be Foil - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:

1. Chemical Composition of C72700

Model	Ni	Sn	Mn	Pb	Zn	Fe	P	Impurities	Cu
C72700	8.5-9.5	5.5-6.5	0.05-0.3	≤0.03	≤0.15	≤0.05	≤0.05	≤0.5	Remnant

2. Physical Properties of C72700

Density	8.9	(g/cm³)
Melting Point	968-1078	(℃)
Thermal Expansion Coefficient	17.25	(X10^-6/℃) 20-200℃
Elastic Modulus	120	(GPa)
Electrical Resistivity at 20℃		μΩ*cm
Quench	≤19.5
Precipitation Hardening	≤15
Electrical Conductivity(IACS,%)		(% IACS)
Electrical Conductivity(IACS,%)	≥9
Precipitation hardening（3 hours）	≥12
Torsional Modulus	50	(GPa)
Thermal Conductivity at 20℃	53.6	(W/m.K)
Bending Fatigue Strength	450 Number of cycles：10⁸	(MPa)

3. Mechanical Properties/State of C72700
1) Rolled Products

State	Hardness	Tensile Strength	Yield Strength	Elongaion	Bending*		Hardness, Elasticity and Bending Fatigue Properties(MPa)
State	HV	Rm (MPa)	Rp 0.2 (MPa)	A50mm (%)	Longitudinal//	Transverse⊥	Longitudinal//	Transverse⊥
Quenching
TB	90-125	420-500	≥200	≥30	0.2	0.2	302	220
Quenching/Cold Rolling
TD1	140-180	460-560	≥300	≥15	0.2	0.2	216	359
TD2	160-200	540-640	≥400	≥10	0.2	0.2	275	390
TD3	200-240	620-720	≥550	≥3	0.5	0.5	444	523
TD4	220-260	700-820	≥600	≈1	2	1	467	568
TDX	≤320	≥780	≥650	≈1	10	2	472	613
Quenching/Precipitation Heat Treatment
TF	230-270	740-860	≥510	≥10	0.5	0.5	566	634
Quenching/Cold Rolling/Precipitation Heat Treatment
TH1	270-310	850-950	≥650	≥8	0.5	0.5	684	724
TH2	290-320	880-980	≥720	≥8	1	1	730	770
TH3	310-340	950-1050	≥800	≥4	1	1	829	≥840
TH4	320-360	1000-1100	≥900	≈3	2	2	≥830	≥840
THX	≤390	≥1050	≥950	≈1	/	/	≥830	≥840
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio

2) Drawn products

State	Hardness	Tensile Strength	Yield Strength	Elongaion	Expansion Coefficient
State	HV	Rm (MPa)	Rp 0.2 (MPa)	A50mm (%)	Z%
Quenching
TB	≤150	400-500	≥200	≥30	≥80
Quenching/Cold Rolling
TD1	150-180	500-580	≥300	≥10	≥75
TD2	180-230	550-720	≥500	≥3	≥70
TD3	220-260	700-800	≥600	≥2	≥65
TD4	230-300	780-880	≥700	≥1.5	≥60
TDX	250-320	880-1000	≥800	≥0.1	≥50

State	HV	Rm (MPa)	Rp 0.2 (MPa)	A50mm (%)	Z%
Quenching/Precipitation Heat Treatment
TF	≤260	770-870	≥500	≥20	≥40
Quenching/Cold Rolling/Precipitation Heat Treatment
TH1	260-300	870-970	≥700	≥13	≥30
TH2	290-310	930-1030	≥800	≥8	≥30
TH3	310-330	1000-1100	≥900	≥5	≥30
TH4	330-360	1100-1200	≥1000	≥2	≥30
THX	≥350	1175-1300	≥1100	≥0.5	≥30

4. Standard Tolerance of Rod and Wire of C72700

Type	Diameter		Tolerance of Diameter		Tolerance of Straightness
Type	inch	mm	inch	mm	inch	mm
Wire	0.2-0.39	6.35-9.9	+/-0.002	+/-0.05	length=10ft,deviation＜0.25 inches	length=3048mm,deviation＜6.35mm
Wire	0.4-0.74	10-18.9	+0.005/-0	+0.13/-0	length=10ft,deviation＜0.25 inches	length=3048mm,deviation＜6.35mm
Rod	0.75-1.6	19-40.9	+0.02/+0.08	+0.5/+2.0	length=10ft,deviation＜0.5 inches	length=3048mm,deviation＜12mm
	1.61-2.75	41-70	+0.02/+0.10	+0.02/+0.10
	2.76-3.25	70.1-82	+0.02/+0.145	+0.02/+0.145
	3.26-6.00	83-152.4	+0.02/+0.187	+0.02/+0.187
	＜0.4	＜10	+/-0.002	+/-0.05

5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts