Factory wholesale C15760 Threadlet - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou
Factory wholesale C15760 Threadlet - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:
1. Chemical Composition of C72700
|
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
|
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
|
Density |
8.9 |
(g/cm3) |
|
Melting Point |
968-1078 |
(℃) |
|
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
|
Elastic Modulus |
120 |
(GPa) |
|
Electrical Resistivity at 20℃ |
|
μΩ*cm |
|
Quench |
≤19.5 |
|
|
Precipitation Hardening |
≤15 |
|
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
|
≥9 |
|
|
|
Precipitation hardening（3 hours） |
≥12 |
|
|
Torsional Modulus |
50 |
(GPa) |
|
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
|
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
|
Quenching |
||||||||
|
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
|
Quenching/Cold Rolling |
||||||||
|
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
|
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
|
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
|
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
|
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
|
Quenching/Precipitation Heat Treatment |
||||||||
|
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
|
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
|
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
|
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
|
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
|
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
|
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
||||||||
2) Drawn products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
|
Quenching |
|||||
|
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
|
Quenching/Cold Rolling |
|||||
|
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
|
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
|
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
|
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
|
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching/Precipitation Heat Treatment |
|||||
|
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
|
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
|
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
|
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
|
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
|
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
|
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
|
inch |
mm |
inch |
mm |
inch |
mm |
|
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation＜0.25 inches |
length=3048mm,deviation＜6.35mm |
|
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
|
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation＜0.5 inches |
length=3048mm,deviation＜12mm |
|
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
|
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
|
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
|
＜0.4 |
＜10 |
+/-0.002 |
+/-0.05 |
|
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts
Product detail pictures:
Related Product Guide:
The key to our success is "Good Product or service High quality, Reasonable Rate and Efficient Service" for Factory wholesale C15760 Threadlet - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: Houston, Guatemala, Hungary, "Make the women more attractive "is our sales philosophy. "Being customers' trusted and preferred brand supplier" is the goal of our company. We are strict with every part of our work. We sincerely welcome friends to negotiate business and start cooperation. We hope to join hands with friends in different industries to create a brilliant future.
By Delia from Romania - 2017.01.28 19:59
We feel easy to cooperate with this company, the supplier is very responsible, thanks.There will be more in-depth cooperation.
By Charlotte from Czech Republic - 2017.11.11 11:41