Factory wholesale C72700 Rod - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou
Factory wholesale C72700 Rod - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:
1. Chemical Composition of C72700
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
Density |
8.9 |
(g/cm3) |
Melting Point |
968-1078 |
(℃) |
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
Elastic Modulus |
120 |
(GPa) |
Electrical Resistivity at 20℃ |
|
μΩ*cm |
Quench |
≤19.5 |
|
Precipitation Hardening |
≤15 |
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
≥9 |
|
|
Precipitation hardening(3 hours) |
≥12 |
|
Torsional Modulus |
50 |
(GPa) |
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
Quenching |
||||||||
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
Quenching/Cold Rolling |
||||||||
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
Quenching/Precipitation Heat Treatment |
||||||||
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
2) Drawn products
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching |
|||||
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
Quenching/Cold Rolling |
|||||
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
Quenching/Precipitation Heat Treatment |
|||||
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
inch |
mm |
inch |
mm |
inch |
mm |
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation<0.25 inches |
length=3048mm,deviation<6.35mm |
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation<0.5 inches |
length=3048mm,deviation<12mm |
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
<0.4 |
<10 |
+/-0.002 |
+/-0.05 |
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts
Product detail pictures:
Related Product Guide:
With our excellent administration, strong technical capability and strict excellent control method, we carry on to offer our clients with responsible good quality, reasonable costs and great companies. We intention at becoming considered one of your most responsible partners and earning your pleasure for Factory wholesale C72700 Rod - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: Germany, New Zealand, Egypt, Our factory is equipped with complete facility in 10000 square meters, which makes us be able to satisfy the producing and sales for most auto part solutions. Our advantage is full category, high quality and competitive price! Based on that, our products win a high admiration both at home and abroad.
By Katherine from Iceland - 2018.11.28 16:25
The customer service staff's attitude is very sincere and the reply is timely and very detailed, this is very helpful for our deal,thank you.
By Emma from Karachi - 2017.10.27 12:12