China New Fashion Design for Cw110c Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou factory and suppliers | Kinkou
English

New Fashion Design for Cw110c Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou

New Fashion Design for Cw110c Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Featured Image
  • New Fashion Design for Cw110c Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou


Download as PDF

Product Detail

Product Tags

Related Video

Feedback (2)

We've been proud with the significant shopper fulfillment and wide acceptance due to our persistent pursuit of top of the range both of those on solution and repair for Cw102c Threadlet , C97 wire , Annealed Copper Wire , Our products are widely used in many industrial fields. Our Company Services Division in good faith for the purpose of the quality of survival. All for customer service.
New Fashion Design for Cw110c Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:

1. Chemical Composition of C72700

Model

Ni

Sn

Mn

Pb

Zn

Fe

P

Impurities

Cu

C72700

8.5-9.5

5.5-6.5

0.05-0.3

≤0.03

≤0.15

≤0.05

≤0.05

≤0.5

Remnant

2. Physical Properties of C72700

Density

8.9

(g/cm3)

Melting Point

968-1078

(℃)

Thermal Expansion Coefficient

17.25

(X10-6/℃) 20-200℃

Elastic Modulus

120

(GPa)

Electrical Resistivity at 20℃

 

μΩ*cm

Quench

≤19.5

 

Precipitation Hardening

≤15

 

Electrical Conductivity(IACS,%)

 

(% IACS)

≥9

 

Precipitation hardening（3 hours）

≥12

 

Torsional Modulus

50

(GPa)

Thermal Conductivity at 20℃

53.6

(W/m.K)

Bending Fatigue Strength

450
Number of cycles：108

(MPa)

3. Mechanical Properties/State of C72700
1) Rolled Products

State

Hardness

Tensile Strength

Yield Strength

Elongaion

Bending*

Hardness, Elasticity and Bending Fatigue Properties(MPa)

HV

Rm (MPa)

Rp 0.2 (MPa)

A50mm (%)

Longitudinal//

Transverse⊥

Longitudinal//

Transverse⊥

Quenching

TB

90-125

420-500

≥200

≥30

0.2

0.2

302

220

Quenching/Cold Rolling

TD1

140-180

460-560

≥300

≥15

0.2

0.2

216

359

TD2

160-200

540-640

≥400

≥10

0.2

0.2

275

390

TD3

200-240

620-720

≥550

≥3

0.5

0.5

444

523

TD4

220-260

700-820

≥600

≈1

2

1

467

568

TDX

≤320

≥780

≥650

≈1

10

2

472

613

Quenching/Precipitation Heat Treatment

TF

230-270

740-860

≥510

≥10

0.5

0.5

566

634

Quenching/Cold Rolling/Precipitation Heat Treatment

TH1

270-310

850-950

≥650

≥8

0.5

0.5

684

724

TH2

290-320

880-980

≥720

≥8

1

1

730

770

TH3

310-340

950-1050

≥800

≥4

1

1

829

≥840

TH4

320-360

1000-1100

≥900

≈3

2

2

≥830

≥840

THX

≤390

≥1050

≥950

≈1

/

/

≥830

≥840

*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio

2) Drawn products

State

Hardness

Tensile Strength

Yield Strength

Elongaion

Expansion Coefficient

HV

Rm (MPa)

Rp 0.2 (MPa)

A50mm (%)

Z%

Quenching

TB

≤150

400-500

≥200

≥30

≥80

Quenching/Cold Rolling

TD1

150-180

500-580

≥300

≥10

≥75

TD2

180-230

550-720

≥500

≥3

≥70

TD3

220-260

700-800

≥600

≥2

≥65

TD4

230-300

780-880

≥700

≥1.5

≥60

TDX

250-320

880-1000

≥800

≥0.1

≥50

 

 

 

 

 

 

State

HV

Rm (MPa)

Rp 0.2 (MPa)

A50mm (%)

Z%

Quenching/Precipitation Heat Treatment

TF

≤260

770-870

≥500

≥20

≥40

Quenching/Cold Rolling/Precipitation Heat Treatment

TH1

260-300

870-970

≥700

≥13

≥30

TH2

290-310

930-1030

≥800

≥8

≥30

TH3

310-330

1000-1100

≥900

≥5

≥30

TH4

330-360

1100-1200

≥1000

≥2

≥30

THX

≥350

1175-1300

≥1100

≥0.5

≥30

4. Standard Tolerance of Rod and Wire of C72700

Type

Diameter

Tolerance of Diameter

Tolerance of Straightness

inch

mm

inch

mm

inch

mm

Wire

0.2-0.39

6.35-9.9

+/-0.002

+/-0.05

length=10ft,deviation＜0.25 inches

length=3048mm,deviation＜6.35mm

0.4-0.74

10-18.9

+0.005/-0

+0.13/-0

Rod

0.75-1.6

19-40.9

+0.02/+0.08

+0.5/+2.0

length=10ft,deviation＜0.5 inches

length=3048mm,deviation＜12mm

1.61-2.75

41-70

+0.02/+0.10

+0.02/+0.10

2.76-3.25

70.1-82

+0.02/+0.145

+0.02/+0.145

3.26-6.00

83-152.4

+0.02/+0.187

+0.02/+0.187

＜0.4

＜10

+/-0.002

+/-0.05

 

 

5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts

Product detail pictures:

New Fashion Design for Cw110c Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou detail pictures

Related Product Guide:
Our commission should be to provide our end users and clients with very best excellent and aggressive portable digital products and solutions for New Fashion Design for Cw110c Bar - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: Ecuador, Jamaica, Burundi, Our products are mainly exported to Europe, Africa, America, the Middle East and Southeast Asia and other countries and regions. We have enjoyed a great reputation among our customers for quality products and good services.We would make friends with businessmen from at home and abroad, following the purpose of "Quality First, Reputation First, the Best Services."
    • This company has a lot of ready-made options to choose and also could custom new program according to our demand, which is very nice to meet our needs.
    5 Stars By Judith from Malaysia - 2018.12.10 19:03
    A good manufacturers, we have cooperated twice, good quality and good service attitude.
    5 Stars By Kim from San Francisco - 2018.04.25 16:46
    Write your message here and send it to us

    related products

    Hit enter to search or ESC to close