Wholesale C15715 Threadlet - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou
Wholesale C15715 Threadlet - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou Detail:
1. Chemical Composition of C72700
|
Model |
Ni |
Sn |
Mn |
Pb |
Zn |
Fe |
P |
Impurities |
Cu |
|
C72700 |
8.5-9.5 |
5.5-6.5 |
0.05-0.3 |
≤0.03 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.5 |
Remnant |
2. Physical Properties of C72700
|
Density |
8.9 |
(g/cm3) |
|
Melting Point |
968-1078 |
(℃) |
|
Thermal Expansion Coefficient |
17.25 |
(X10-6/℃) 20-200℃ |
|
Elastic Modulus |
120 |
(GPa) |
|
Electrical Resistivity at 20℃ |
|
μΩ*cm |
|
Quench |
≤19.5 |
|
|
Precipitation Hardening |
≤15 |
|
|
Electrical Conductivity(IACS,%) |
|
(% IACS) |
|
≥9 |
|
|
|
Precipitation hardening（3 hours） |
≥12 |
|
|
Torsional Modulus |
50 |
(GPa) |
|
Thermal Conductivity at 20℃ |
53.6 |
(W/m.K) |
|
Bending Fatigue Strength |
450 |
(MPa) |
3. Mechanical Properties/State of C72700
1) Rolled Products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Bending* |
Hardness, Elasticity and Bending Fatigue Properties(MPa) |
||
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Longitudinal// |
Transverse⊥ |
Longitudinal// |
Transverse⊥ |
|
|
Quenching |
||||||||
|
TB |
90-125 |
420-500 |
≥200 |
≥30 |
0.2 |
0.2 |
302 |
220 |
|
Quenching/Cold Rolling |
||||||||
|
TD1 |
140-180 |
460-560 |
≥300 |
≥15 |
0.2 |
0.2 |
216 |
359 |
|
TD2 |
160-200 |
540-640 |
≥400 |
≥10 |
0.2 |
0.2 |
275 |
390 |
|
TD3 |
200-240 |
620-720 |
≥550 |
≥3 |
0.5 |
0.5 |
444 |
523 |
|
TD4 |
220-260 |
700-820 |
≥600 |
≈1 |
2 |
1 |
467 |
568 |
|
TDX |
≤320 |
≥780 |
≥650 |
≈1 |
10 |
2 |
472 |
613 |
|
Quenching/Precipitation Heat Treatment |
||||||||
|
TF |
230-270 |
740-860 |
≥510 |
≥10 |
0.5 |
0.5 |
566 |
634 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
||||||||
|
TH1 |
270-310 |
850-950 |
≥650 |
≥8 |
0.5 |
0.5 |
684 |
724 |
|
TH2 |
290-320 |
880-980 |
≥720 |
≥8 |
1 |
1 |
730 |
770 |
|
TH3 |
310-340 |
950-1050 |
≥800 |
≥4 |
1 |
1 |
829 |
≥840 |
|
TH4 |
320-360 |
1000-1100 |
≥900 |
≈3 |
2 |
2 |
≥830 |
≥840 |
|
THX |
≤390 |
≥1050 |
≥950 |
≈1 |
/ |
/ |
≥830 |
≥840 |
|
*:According to DIN 5011(25/10/85),bending 90 ° along the rolling direction, divide the minimum bending radius by the thickness to determine the R /t ratio |
||||||||
2) Drawn products
|
State |
Hardness |
Tensile Strength |
Yield Strength |
Elongaion |
Expansion Coefficient |
|
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
|
Quenching |
|||||
|
TB |
≤150 |
400-500 |
≥200 |
≥30 |
≥80 |
|
Quenching/Cold Rolling |
|||||
|
TD1 |
150-180 |
500-580 |
≥300 |
≥10 |
≥75 |
|
TD2 |
180-230 |
550-720 |
≥500 |
≥3 |
≥70 |
|
TD3 |
220-260 |
700-800 |
≥600 |
≥2 |
≥65 |
|
TD4 |
230-300 |
780-880 |
≥700 |
≥1.5 |
≥60 |
|
TDX |
250-320 |
880-1000 |
≥800 |
≥0.1 |
≥50 |
|
|
|
|
|
|
|
|
State |
HV |
Rm (MPa) |
Rp 0.2 (MPa) |
A50mm (%) |
Z% |
|
Quenching/Precipitation Heat Treatment |
|||||
|
TF |
≤260 |
770-870 |
≥500 |
≥20 |
≥40 |
|
Quenching/Cold Rolling/Precipitation Heat Treatment |
|||||
|
TH1 |
260-300 |
870-970 |
≥700 |
≥13 |
≥30 |
|
TH2 |
290-310 |
930-1030 |
≥800 |
≥8 |
≥30 |
|
TH3 |
310-330 |
1000-1100 |
≥900 |
≥5 |
≥30 |
|
TH4 |
330-360 |
1100-1200 |
≥1000 |
≥2 |
≥30 |
|
THX |
≥350 |
1175-1300 |
≥1100 |
≥0.5 |
≥30 |
4. Standard Tolerance of Rod and Wire of C72700
|
Type |
Diameter |
Tolerance of Diameter |
Tolerance of Straightness |
|||
|
inch |
mm |
inch |
mm |
inch |
mm |
|
|
Wire |
0.2-0.39 |
6.35-9.9 |
+/-0.002 |
+/-0.05 |
length=10ft,deviation＜0.25 inches |
length=3048mm,deviation＜6.35mm |
|
0.4-0.74 |
10-18.9 |
+0.005/-0 |
+0.13/-0 |
|||
|
Rod |
0.75-1.6 |
19-40.9 |
+0.02/+0.08 |
+0.5/+2.0 |
length=10ft,deviation＜0.5 inches |
length=3048mm,deviation＜12mm |
|
1.61-2.75 |
41-70 |
+0.02/+0.10 |
+0.02/+0.10 |
|||
|
2.76-3.25 |
70.1-82 |
+0.02/+0.145 |
+0.02/+0.145 |
|||
|
3.26-6.00 |
83-152.4 |
+0.02/+0.187 |
+0.02/+0.187 |
|||
|
＜0.4 |
＜10 |
+/-0.002 |
+/-0.05 |
|
|
|
5. Application of C72700
Substituting beryllium copper alloy
It is used for glasses, electricians, electromechanical, electronics, connectors, automobiles, household appliances, spectade industry, turning parts
Product detail pictures:
Related Product Guide:
"Based on domestic market and expand abroad business" is our progress strategy for Wholesale C15715 Threadlet - KINKOU-96 copper alloy(Cu-9Ni-6Sn C72700) – Kinkou , The product will supply to all over the world, such as: Argentina, New Zealand, Singapore, Our company adheres to the spirit of "lower costs, higher quality, and making more benefits for our clients". Employing talents from the same line and adhering to the principle of "honesty, good faith, real thing and sincerity", our company hopes to gain common development with clients from both at home and abroad!
By Kitty from Manila - 2018.04.25 16:46
High Quality, High Efficiency, Creative and Integrity, worth having long-term cooperation! Looking forward to the future cooperation!
By Edwina from Cologne - 2018.06.18 17:25